　　Study on Galvanic Corrosion in Cyclic Wet-dry Immersion Test of 7A52 Aluminium Alloy

　　WANG Wei  HUANG Yan-bin XU Ke-ke

　?。ˋcademy of Armored Forces Engineering,Beijing 100072;）

　　Abstract: In this paper, The galvanic corrosion of 7A52 in after cyclic wet-dry immersion is been studied. We have studied 38CrSi and 5A06 that often been used arrange in pairs or groups with 7A52 .The galvanic current and galvanic voltage of two different materials is been tested. We have studied the surface of samples after corrosion use SEM. We can get that in cyclic wet-dry immersion , the structure of corrosion product is loose and more gap , the corrosion rate is more serious.

　　Key words:7A52; galvanic corrosion;cyclic wet-dry immersion test

　　聯(lián)系方式

　　徐可可：ly20042089@126.com

責(zé)任編輯：趙澤南

《中國(guó)腐蝕與防護(hù)網(wǎng)電子月刊》征訂啟事
投稿聯(lián)系：劉娟 電話：010-82387968-807
QQ: 2850329508 郵箱：liujuan@ecorr.org
中國(guó)腐蝕與防護(hù)網(wǎng)官方 QQ群：140808414